MULTIFILL 2-5 is a cement-based, colored tile grout. It offers high mechanical strength and color stability. Suitable for joint width 2-5 mm._x000D_It is classified as type CG2 WA tile grout according to EN 13888._x000D__x000D_Fields of application_x000D_MULTIFILL 2-5 is used for pointing tile joints on walls or floors, for indoor and outdoor applications._x000D__x000D_Technical data_x000D_Form: cementitious powder_x000D_Colors: 24_x000D_Water demand: 6,50 l/25 kg bag_x000D_Bulk density of dry mortar: 1,25 0,40 kg/l_x000D_Bulk density of fresh mortar: 1,60 0,50 kg/l_x000D_Application temperature: from +5°C to +35°C_x000D_Abrasion resistance: ≤ 1000 mm3_x000D_(ΕΝ 12808-2)_x000D_Compressive strength after:_x000D_• 28 days: 40,00 N/mm2_x000D_• 25 freeze-thaw cycles: 40,00 N/mm2_x000D_(ΕΝ 12808-3)_x000D_Flexural strength after:_x000D_• 28 days: 6,00 N/mm2_x000D_• 25 freeze-thaw cycles: 5,00 N/mm2_x000D_(ΕΝ 12808-3)_x000D_Drying shrinkage: ≤ 2mm/m_x000D_(ΕΝ 12808-4)_x000D_Water absorption after:_x000D_• 30 min: ≤ 2 g_x000D_• 240 min: ≤ 5 g_x000D_(ΕΝ 12808-5)_x000D_Pot life: at least 4 h at +20°C_x000D_Walkability: after 10 h at +20°C_x000D__x000D_Directions for use_x000D__x000D_1. Substrate_x000D_The substrate covered with tiles should be perfectly clean. The joints should be carefully_x000D_cleaned and dampened with a wet sponge._x000D__x000D_2. Application_x000D_MULTIFILL 2-5 is added to water under continuous stirring, until a uniform paste is_x000D_formed. A low revolution mixer is recommended for the mixing. The mixture should be left about 3 minutes to_x000D_settle and then slightly stirred again. Spread the grout on to the joints, using a rubber float in a diagonal direction to the_x000D_joints, in order to fill them completely. The excess material should be wiped after a while, using a wet sponge. Finally, the surface may_x000D_be cleaned with a dry cloth. Outdoors or at high temperatures repeated dampening is recommended after a few hours_x000D_and when the grout has dried._x000D__x000D_CONSUMPTION_x000D_0.2-2.0 kg/m², depending on tile size and joint width.